New Methods for Corrosion Testing of Aluminum Alloys
- ISBN-10
- 0803114354
- ISBN-13
- 9780803114357
- Category
- Aluminum alloys
- Pages
- 219
- Language
- English
- Published
- 1992
- Publisher
- ASTM International
- Author
- Vinod S. Agarwala
Description
Evaluates the usefulness of the current standards on exfoliation and corrosion testing of aluminum alloys and their applicability to new requirements and advanced alloys. The 13 papers, from an international symposium in San Francisco, May 1990, discuss whether the existing standards should be revis
Get the book
Similar books
-
Fatigue and Fracture Mechanics: 27th Volume
By Robert S. PiascikREFERENCE: Rudland, D. L. and Brust, F., "The Effect of Cyclic Loading During Ductile Tearing on the Fracture Resistance of ... They suggest that in order to account for fatigue crack growth, 1 Research scientist and senior research ...
-
Testing of Metallic and Inorganic Coatings: A Symposium Sponsored by ASTM Committee B-8 on Metallic and Inorganic Coatings, Chicago, IL,...
By William B. HardingA Symposium Sponsored by ASTM Committee B-8 on Metallic and Inorganic Coatings, Chicago, IL, 14-15 April 1986 William B. ... REFERENCE: Lacey, E. A. and Sonnino, C, "Testing of Anodic Coatings on Aluminum Alloys: A Review," Testing of ...
-
Fractography in Failure Analysis: A Symposium Presented at May Committee Week, American Society for Testing and Materials, 1-6 May 1977,...
By Bernard M. Strauss, W. H. CullenFractography in Failure Analysis: A Symposium Presented at May Committee Week, American Society for Testing and Materials, 1-6 May 1977,...
-
Formability of Metallic Materials-2000 A.D.
By John R. Newby, B. A. Niemeier5000 Vo = 3.38 m / sec -115 ° C 4000 아 -100 ° C -70 ° C - -20 ° C 3000F 25 ° C LOAD , N 25 ° C 2000F C5 - DUAL PHASE STEEL 1000F 1.25 1.50 .25 .5 .75 | TIME , m sec INCREASING DISPLACEMENT FIG . 5b - Instrumented impact traces for the ...
-
Fatigue Testing and Analysis Under Variable Amplitude Loading Conditions
By Peter C. McKeighan, Narayanaswami Ranganathan[45] Sunder, R., "Contribution of Individual Spectrum Load Cycles to Damage in Notch Root Crack Initiation, Short and Long Crack Growth," In: Advances in Fatigue Lifetime Predictive Techniques: Second Volume, ASTM STP 1211, ...
-
Fracture Mechanics: 26th Volume
By Walter G. ReuterParida, B.K. and Nicholas, T., "Influence of Crack Closure and Stress Ratio on Near-Threshold Fatigue Crack Growth Behavior in Ti-1100," Cyclic Deformation. Fracture, and Nondestructive Evaluation of Advanced Materials: Second Volume.
-
Extrusion: Second Edition
Extrusion: Second Edition
-
Engine Coolant Testing, Third Volume
By Roy E. BealCurrently, acceptable performance in the critical problem areas discussed previously is mainly established through full-scale engine testing. Specifications based on full-scale engine tests would tend to reduce the participation of many ...
-
Casting defects handbook: Aluminium and Aluminium alloys
By David V. NeffCasting defects handbook: Aluminium and Aluminium alloys
-
Introduction to Aluminum Alloys and Tempers
By J. Gilbert KaufmanAnnotation Examines characteristics of wrought and cast aluminum alloys, then presents basic aluminum alloy and temper designation systems, as developed by the Aluminum Association, and explains them with examples.