Zur Schädigungsentwicklung bei der Korrosionsermüdung von Aluminiumbasislegierungen mit definierten fertigungsbedingten Randschichtzuständen
- ISBN-10
- 386219468X
- ISBN-13
- 9783862194681
- Category
- Aluminum alloys
- Pages
- 280
- Language
- German
- Published
- 2013
- Publisher
- kassel university press GmbH
- Author
- Klaus Timmermann
Description
... der Korrosionsermüdung von Aluminiumbasislegierungen mit definierten fertigungsbedingten Randschichtzuständen Der Bauschingereffekt bei vergüteten, bainitischen und normalisierten Zuständen der Stähle 42CrMoS4 und 100Cr6.
Get the book
Similar books
-
Fatigue and Fracture Mechanics: 27th Volume
By Robert S. PiascikREFERENCE: Rudland, D. L. and Brust, F., "The Effect of Cyclic Loading During Ductile Tearing on the Fracture Resistance of ... They suggest that in order to account for fatigue crack growth, 1 Research scientist and senior research ...
-
Testing of Metallic and Inorganic Coatings: A Symposium Sponsored by ASTM Committee B-8 on Metallic and Inorganic Coatings, Chicago, IL,...
By William B. HardingA Symposium Sponsored by ASTM Committee B-8 on Metallic and Inorganic Coatings, Chicago, IL, 14-15 April 1986 William B. ... REFERENCE: Lacey, E. A. and Sonnino, C, "Testing of Anodic Coatings on Aluminum Alloys: A Review," Testing of ...
-
Fractography in Failure Analysis: A Symposium Presented at May Committee Week, American Society for Testing and Materials, 1-6 May 1977,...
By Bernard M. Strauss, W. H. CullenFractography in Failure Analysis: A Symposium Presented at May Committee Week, American Society for Testing and Materials, 1-6 May 1977,...
-
Formability of Metallic Materials-2000 A.D.
By John R. Newby, B. A. Niemeier5000 Vo = 3.38 m / sec -115 ° C 4000 아 -100 ° C -70 ° C - -20 ° C 3000F 25 ° C LOAD , N 25 ° C 2000F C5 - DUAL PHASE STEEL 1000F 1.25 1.50 .25 .5 .75 | TIME , m sec INCREASING DISPLACEMENT FIG . 5b - Instrumented impact traces for the ...
-
Fatigue Testing and Analysis Under Variable Amplitude Loading Conditions
By Peter C. McKeighan, Narayanaswami Ranganathan[45] Sunder, R., "Contribution of Individual Spectrum Load Cycles to Damage in Notch Root Crack Initiation, Short and Long Crack Growth," In: Advances in Fatigue Lifetime Predictive Techniques: Second Volume, ASTM STP 1211, ...
-
Fracture Mechanics: 26th Volume
By Walter G. ReuterParida, B.K. and Nicholas, T., "Influence of Crack Closure and Stress Ratio on Near-Threshold Fatigue Crack Growth Behavior in Ti-1100," Cyclic Deformation. Fracture, and Nondestructive Evaluation of Advanced Materials: Second Volume.
-
New Methods for Corrosion Testing of Aluminum Alloys
By Vinod S. AgarwalaREFERENCE: Rosales, B. M., Ayllon, E. S., and Leiro, M. C, "Accelerated Test for Determining Microbiological-Influenced Corrosion Resistance of Aluminum Alloys," New Methods for Corrosion Testing of Aluminum Alloys, ASTM STP 1134, ...
-
Extrusion: Second Edition
Extrusion: Second Edition
-
Engine Coolant Testing, Third Volume
By Roy E. BealCurrently, acceptable performance in the critical problem areas discussed previously is mainly established through full-scale engine testing. Specifications based on full-scale engine tests would tend to reduce the participation of many ...
-
Casting defects handbook: Aluminium and Aluminium alloys
By David V. NeffCasting defects handbook: Aluminium and Aluminium alloys